Aluminum 3104-H19 Categories: Metal; Nonferrous Metal; Aluminum Alloy; 3000 Series Aluminum Alloy. Material Notes: Data points with the AA note have been provided by the Aluminum Association, Inc. and are NOT FOR DESIGN. Composition Notes: Composition information provided by the Aluminum Association and is not for design.
3104 (AlMn1Mg1Cu) Aluminum 3104 aluminum is a 3000-series aluminum alloy: the main alloying addition is manganese, and it is formulated for primary forming into wrought products. 3104 is the Aluminum Association (AA) designation for this material.
3104-H19 aluminum is 3104 aluminum in the H19 temper. To achieve this temper, the metal is strain hardened to a strength that exceeds H18 by at least 10 MPa (or 1.5 ksi). The graph bars on the material properties cards below compare 3104-H19 aluminum to: 3000-series alloys (top), all aluminum alloys (middle), and the entire database (bottom).
Hardness, Vickers 88 88 Converted from Brinell Hardness Value Tensile Strength, Ultimate 290 MPa 42100 psi Tensile Strength, Yield 260 MPa 37700 psi Elongation at Break 4.00 % 4.00 % In 5 cm; Sample 1.6 mm thick Modulus of Elasticity 69.0 GPa 10000 ksi Average of Tension and Compression. In Aluminum alloys, the
Alloy 3104 H19 Aluminum For Can Stock, Alloy 3104... Alloy 3104 H19 Aluminum For Can Stock, Wholesale Various High Quality Alloy 3104 H19 Aluminum For Can Stock Products from Global Alloy 3104 H19 Aluminum For Can Stock ... Chat Now Send Inquiry; 3000 Series Aluminum Alloys - Mandel Metals. 3000 Series Aluminum Alloys. Manganese is the major alloying element in this group. ... 3104 Aluminum Alloy.
Alloy 3104 H19 Aluminum For Can Stock, Wholesale Various High Quality Alloy 3104 H19 Aluminum For Can Stock Products from Global Alloy 3104 H19 Aluminum For Can Stock ... Chat Now Send Inquiry; Aluminum 3104 H19 for can stock - Alibaba. Aluminum 3104 H19 for can stock,US $ 2,700 - 4,000 / Metric Ton, 3000 Series, H19, Plate.Source from Jinan Honesty Aluminum Industry Co., Ltd. on Alibaba.com.
Aluminium / Aluminum 3004 alloy is a non-heat treatable alloy. Forging. Aluminium / Aluminum 3004 alloy is forged at temperatures ranging from 372 to 510°C (700 to 950°F). Hot Working. Aluminium / Aluminum 3004 alloy is hot worked at 260 to 483°C (500 to 900°F). Cold Working. Aluminium / Aluminum 3004 alloy can be cold worked up to 75% reduction of area using conventional techniques.
3004 aluminium alloy is an alloy in the wrought aluminium-manganese family (3000 or 3xxx series). It is similar to the 3003 alloy , except for the addition of approximately 1% magnesium. It can be cold worked (but not, unlike some other types of aluminium alloys, heat treated ) to produce tempers with a higher strength but a lower ductility.
Some aluminum alloys can match or even exceed the strength of common construction steel. Aluminum retains its toughness at very low temperatures, without becoming brittle like carbon steels. Aluminum is a good conductor of heat and electricity.
Alloy 4043 is one of the most widely used filler alloys for welding 6xxx series alloys for structural and automotive applications. 5xxx Series Magnesium is the primary alloying agent in the 5xxx series and is one of the most effective and widely used alloying elements for aluminum.